3Cr12 3mm Stainless Steel Sheets / SS Plate Cold Rolled for Food industry
QuickDetail:
Produce standard: ASTM, AISI, JIS, DIN, GB
Material: 201 202 304 304L 316L 317L 309S 310S 316Ti 321 409L 410 410S
420 420J1 420J2 430 439 444 446 3Cr12 904L S31803 S32205 etc.
Thickness-Cold Rolled:0.3, 0.4, 0.5, 0.6, 0.7, 0.8, 1.0, 1.2, 1.5, 2.0, 3.0, 4.0, 5.0mm
Thickness-HotRolled:3.0, 4.0, 5.0, 6.0, 8.0, 10.0...70mm Or As Required
Width:1000mm, 1219mm, 1500mm, 1800mm, 2000mm
Package: PVC protective film+craft paper+metal pallet or as requirement.
Trade terms: EXW, FOB, CFR, CIF
Description:
Thickness:Cold Rolled: 0.3, 0.4, 0.5, 0.6, 0.7, 0.8, 1.0, 1.2, 1.5, 2.0, 3.0, 4.0, 5.0mm
Hot Rolled: 3.0, 4.0, 5.0, 6.0, 8.0, 10.0...70mm Or As Required
Width: 1000mm, 1219mm, 1500mm, 1800mm, 2000mm
Length: 1m-12m OrAccording to customers request
Material: 201 202 304 304L 316L 317L 309S 310S 316Ti 321 409L 410 410S
420 420J1 420J2 430 439 444 446 3Cr12 904L S31803 S32205 etc.
Technique: Hot/Cold Rolled
Surface finish:2B, 2D, BA, HL(Hair Line), No. 1, No. 3, No. 4, No. 7, Mirror(8K),
Gold mirror, Black mirror etc.
Quality Control: Mill Test Certificate, SGS Or Other Third Party Inspection Also Is Acceptable.
Application: Construction, Machine Building, Container Manufacturing, Shipbuilding, Bridges etc.
Marking:Registeredlogo,HeatNumber,SteelGrade,Standard,Size
3Cr12 ferritic stainless steel is widely used in the field of the South African development of 3 cr12 containing 12%Cr ferriteStainless steel, equivalent to 1.4003 of European brand, is a kind of used to replace coating, weathering steel and carbon steelAluminum economical ferritic stainless steel.It is simple in processing and manufacturing, the characteristics of the conventional welding technology, welding has been widely used in recent years.Once introduced 3 cr12 in the application of railway freight cars.Now introduce it in the sugar industry, power plant cooling tower, water treatment, civil stockade, utility poles, bus chassis, and other fields of application.
| Grade | ChemicalComposition | ||||||||
| AIST | EN | C | Si | Mn | P | S | Ni | Cr | Others |
| UNS | max | max | max | max | max | max | |||
| Austeniticstainlesssteels | |||||||||
| 201 | ** | 0.15 | 1 | 5.5-7.5 | 0.06 | 0.03 | 1 | 16.00-18.00 | N0.25 |
| 202 | ** | 0.15 | 1 | 7.5-10 | 0.06 | 0.03 | 4.00-6.00 | 17.00-19.00 | N0.25 |
| 301 | 1.431 | 0.15 | 1 | 2 | 0.045 | 0.03 | 6.00-8.00 | 16.00-18.00 | _ |
| 301L | 1.4318 | 0.03 | 1 | 2 | 0.045 | 0.03 | 6.00-8.00 | 16.00-18.00 | N:0.20 |
| 304 | 1.4301 | 0.08 | 1 | 2 | 0.045 | 0.03 | 8.0-10.50 | 18.00-20.00 | _ |
| 304L | 1.4307 | 0.03 | 1 | 2 | 0.045 | 0.03 | 9.00-13.00 | 18.00-20.00 | _ |
| 316 | 1.4401 | 0.08 | 1 | 2 | 0.045 | 0.03 | 10.00-14.00 | 16.00-18.00 | Mo:2.00-3.00 |
| 316L | 1.4404 | 0.03 | 1 | 2 | 0.045 | 0.03 | 10.00-14.00 | 16.00-18.00 | Mo:2.00-3.00 |
| 321 | 1.4541 | 0.08 | 1 | 2 | 0.045 | 0.03 | 9.00-13.00 | 17.00-19.00 | Ti:5*C% |
| 309S | 1.4833 | 0.08 | 1 | 2 | 0.045 | 0.03 | 12.00-15.00 | 22.00-24.00 | _ |
| 310S | 1.4845 | 0.08 | 1.5 | 2 | 0.045 | 0.03 | 19.00-22.00 | 24.00-26.00 | _ |
| Ferriticstainlesssteels | |||||||||
| 409L | 1.4512 | 0.03 | 1 | 1 | 0.04 | 0.03 | _ | 10.50-11.75 | Ti:6*C%-0.75 |
| 410 | 1.4006 | 0.15 | 1 | 1 | 0.04 | 0.03 | _ | 11.50-13.50 | _ |
| 410L | 1.4003 | 0.03 | 1 | 1 | 0.04 | 0.03 | _ | 11.00-13.50 | _ |
| 439 | 1.451 | 0.03 | 1 | 1 | 0.04 | 0.03 | 0.5 | 17.00-19.00 | Ti:(0.20+4*(C+N()-1.10,Al:0.15:N:0.030 |
| 434 | 1.4113 | 0.12 | 1 | 1 | 0.04 | 0.03 | _ | 16.00-18.00 | _ |
| 444 | 1.4521 | 0.025 | 1 | 1 | 0.04 | 0.03 | _ | 17.00-20.00 | Mo:1.75-2.50Ti,Nb,Zr:8*(C%+N%)-0.80 |
| 430 | 1.4016 | 0.12 | 1 | 1 | 0.04 | 0.03 | _ | 16.00-18.00 | _ |
| Martensiticstainlesssteels | |||||||||
| 420 | 1.4021 | 0.16-0.25 | 1 | 1 | 0.04 | 0.03 | _ | 12.00-14.00 | _ |
| 420JS | 1.4028 | 0.26-0.40 | 1 | 1 | 0.04 | 0.03 | _ | 12.00-14.00 | _ |
| Grade | MechanicalProperties | |||||
| AIST | EN | YieldStrength | Tensile | Elongation | Hardness | |
| UNS | N/mm2 | N/mm2 | % | HV | HRB | |
| Austeniticstainlesssteels | ||||||
| 201 | ** | 245 | 640 | 40 | 253 | 100 |
| 202 | ** | 245 | 590 | 40 | 218 | 95 |
| 301 | 1.431 | ≥205 | ≥520 | ≥40 | ≤218 | ≤95 |
| 301L | 1.4318 | ≥215 | ≥550 | ≥45 | ≤218 | ≤95 |
| 304 | 1.4301 | ≥205 | ≥520 | ≥40 | ≤200 | ≤90 |
| 304L | 1.4307 | ≥175 | ≥480 | ≥40 | ≤200 | ≤90 |
| 316 | 1.4401 | ≥205 | ≥520 | ≥40 | ≤200 | ≤90 |
| 316L | 1.4404 | ≥175 | ≥480 | ≥40 | ≤200 | ≤90 |
| 321 | 1.4541 | ≥205 | ≥520 | ≥40 | ≤200 | ≤90 |
| 309S | 1.4833 | ≥205 | ≥520 | ≥40 | ≤200 | ≤90 |
| 310S | 1.4845 | ≥205 | ≥520 | ≥40 | ≤200 | ≤90 |
| Ferriticstainlesssteels | ||||||
| 409L | 1.4512 | ≥175 | ≥360 | ≥25 | ≤175 | ≤80 |
| 410 | 1.4006 | ≥205 | ≥440 | ≥20 | ≤210 | ≤93 |
| 410L | 1.4003 | ≥195 | ≥360 | ≥22 | ≤200 | ≤88 |
| 439 | 1.451 | ≥205 | ≥415 | ≥22 | ≤200 | ≤89 |
| 434 | 1.4113 | ≥205 | ≥450 | ≥22 | ≤200 | ≤88 |
| 444 | 1.4521 | ≥245 | ≥410 | ≥20 | ≤230 | ≤96 |
| 430 | 1.4016 | ≥205 | ≥420 | ≥22 | ≤200 | ≤88 |
| Martensiticstainlesssteels | ||||||
| 420 | 1.4021 | ≥225 | ≥520 | ≥18 | ≥234 | ≥97 |
| 420JS | 1.4028 | ≥225 | ≥540 | ≥18 | ≥247 | ≥99 |